AMS 5662 Nickel Chromium Alloy Inconel 600 Bar With Corrosion Resistance
Product Introduction
Inconel 600 rod (bar) is a high-performance Ni Cr Fe based solid solution strengthened alloy bar with excellent high-temperature strength, oxidation resistance and corrosion resistance. Its main components include nickel (more than 72%), chromium (14% -17%) and iron (6% -10%), which give Inconel 600 rod excellent corrosion resistance, especially in high temperature and corrosive environment. Inconel 600 rod can maintain good mechanical properties at temperatures up to 1093 ° C (2000 ° f), including high strength and creep resistance. Its excellent corrosion resistance enables it to perform well in a variety of corrosive environments, including seawater, acidic solutions and alkaline solutions. Inconel 600 rod is widely used in aerospace, chemical, energy, nuclear and other fields. It is used to manufacture high-temperature components such as combustion chambers, nozzles, turbine blades and fasteners of aircraft engines, as well as components such as pumps, valves and pipes in nuclear power plants.
Parameter
Chemical Properties of Inconel 600
| C | Cr | Ni+Co | Al | Ti | Fe | Nb+Ta | Mn | Si | P | S | Cu |
| ≤0.15 | 14.0～17.0 | ≥72 | ≤0.35 | ≤0.50 | 6.0～10.0 | ≤1.0 | ≤1.0 | ≤0.5 | ≤0.04 | ≤0.015 | ≤0.5 |
| ITEM | θ/℃ | TENSIE STRENGTH | HBS |
| σb/MPa | σP0.2/MPa | δ5/% | φ/% |
| BAR/ROD | 20 | ≥585 | ≥240 | ≥30 | - | 134～217 |
| RING | 20 | ≥520 | ≥205 | ≥35 | - | ≥187 |
| HOT ROLL PLATE | 20 | ≥550 | ≥240 | ≥35 | ≥40 | - |
| 900 | ≥95 | ≥45 | ≥40 | ≥50 | - |
| COLD ROLLED SHEET | 20 | ≥550 | ≥240 | ≥30 | - | - |
| 900 | ≥90 | ≥40 | ≥60 | - | - |
| COLD ROLLED SHEET | 20 | ≥550 | ≥200 | ≥30 | - | - |
| STRIP | 20 | ≥550 | ≥240 | ≥30 | - | - |
| WIRE | 20 | | | | - | HV≤151 |
| Shape | Size(mm) |
| WIre | 0.5-7.5 |
| Rod/Bar | 8.0-200 |
| Strip | (0.5-2.5)*(5-180) |
| Tube | custom made |
| Plate | custom made |
Specific Applications
Inconel 600 rod is a high-performance nickel based alloy with excellent corrosion resistance and high temperature strength, which is widely used in the following major industrial fields:
- Aerospace:It is used to manufacture high-temperature components and engine components of aero-engine. These components need to operate in harsh environments such as high temperature, high pressure and strong corrosion for a long time.
- Chemical industry:It is used to manufacture chemical equipment, such as reactors, heat exchangers, tanks, etc., which work in high temperature and corrosive environment.
- Nuclear energy:It is used to manufacture structures and components in nuclear reactors and is trusted for its stability in high radiation environments.
- Energy:It is used to manufacture heat exchangers and condensers in power plants. These equipment need to operate stably in high temperature and corrosive environment for a long time.
Advantages and Characteristics
- Excellent corrosion resistance:Inconel 600 has excellent corrosion resistance and can be used for a long time in oxidation, acid, alkaline and chloride environment.
- Excellent high temperature strength:Inconel 600 still has good strength and rigidity in high temperature environment, and can maintain stable mechanical properties at temperatures up to 700 ° C.
- Good oxidation resistance:Inconel 600 has good oxidation resistance in high temperature oxidation environment, and can form dense oxide film at high temperature to effectively prevent corrosion.
- Excellent fatigue resistance:Inconel 600 has excellent fatigue resistance and can be used for a long time under a wide range of cyclic loads.
- Good processability:Inconel 600 has good cold forming characteristics and can be processed by common processing technologies, such as forging, rolling, bending, etc.
Contact Us
Email:fbwlau@cnrunlai.com
Oem service:
Welcome customized size
We are experience factory for OEM&ODM service
Related Questions and Answers
What are the main components of Inconel 600?
The main components of Inconel 600 are nickel (72%), chromium (14-17%), iron (6-10%), carbon (≤ 0.15%), manganese (≤ 1%), silicon (≤ 0.5%), copper (≤ 0.5%), phosphorus (≤ 0.015%), and sulfur (≤ 0.015%).
What is the corrosion resistance of Inconel 600?
Inconel 600 has excellent corrosion resistance, especially in high temperature sulfur atmosphere. Its high chromium and nickel content enables it to form a dense oxide film at high temperature, effectively preventing corrosion.
What is the high temperature strength of Inconel 600?
Inconel 600 can still maintain good mechanical properties in high temperature environment. After annealing, the tensile strength can reach 650 n/mm ², the yield strength can reach 300 n/mm ², and the elongation can reach 30%. At 700 ° C, the tensile strength can still be maintained above 500 MPa.
What is the processability of Inconel 600?
Inconel 600 has good machinability. Although its high strength makes machining relatively difficult, it can still realize the manufacturing of complex parts through reasonable processing technology and tool selection. In the market, many enterprises have developed special processing tools for Inconel 600 to improve processing efficiency.